Description
| Item | Test method | Unit | Data | |
| Density | 1S01183 | g/cm3 | 0.95 | |
| VA content | TGA | % | 26-33 | |
| Softening point | DSC | ℃ | 55 | |
| Surace hardness | GB/T531-1999 | Shore A | 65 | |
| Tensile strenghth (after crosslinking) | IS0527-3 | MPa | 20 | |
| Elongation (after crosslinking) | % | 600 | ||
| Strenghth of Extension | MPa | 6 | ||
| UV cutoff wavelength | UV-vis | Nm | 360 | |
| Optical transmission | GB2410-80 | % | 91 | |
| Refractive index | 1SO489 | 1.482 | ||
| Theral shrinkage (0.45MM: pre-crosslinking test, 120℃,3min ) |
Q/ZX001-2012 | MD% | ≤3.0 | |
| TD% | ≤1.0 | |||
| Cross-linking rate (140℃，17min) | Q/ZX001-2012 | Gel% | ≥75.0 | |
| Peeling strength | With Glass | Q/ZX001-2012 | N/cm | >60 |
| With TPT | N/cm | >40 | ||
| Damp Heat resistance(90℃,90%RH, 1500hrs) |
Yellowness index | Q/ZX001-2012 | △YI | <3 |
| Peeling strenghth with glass |
N/cm | >40 | ||
| Volume resistance | GB/T 1410 | Ω·cm | ≥1*1015 | |
| Dielectric strength | GB/T1408.1 | Kv/mm | >28 | |
| PlD resistance test (85℃,85%RH.-1000V.96H) |
IEC61730-2:2004 IEC61215:2005 |
Power loss % | <5% | |